Enhancement of magnetoresistance in manganite multilayers

Magnanite multilayers have been fabricated using La0.67Ca0.33MnO3 as the ferromagnetic layer and Pr0.7Ca0.3MnO3 and Nd0.5Ca0.5MnO3 as the spacer layers. All the multilayers were grown on LaAlO3 (100) by pulse laser deposition. An enhanced magnetoresistnace (defined (RH- R0)/R0) of more than 98% is observed in these multilayers. Also a low field magnetoresistance of 41% at 5000 Oe is observed in these multilayer films. The enhanced MR is attributed to the induced double exchange in the spacer layer, which is giving rise to more number of conducting carriers. This is compared by replacing the spacer layer with LaMnO3 where Mn exists only in 3+ state and no enhancement is observed in the La0.67Ca0.33MnO3 / LaMnO3 multilayers as double exchange mechanism can not be induced by external magnetic fields.Comment: 13 pages, 5 Figure

Scanning Raman spectroscopy for characterizing compositionally spread films

Composition-spread La1-xSrxMnO3 thin films were prepared by pulsed laser deposition technique from LaMnO3 and SrMnO3 targets. The films were epitaxial with a continuous variation of the out-of-plane lattice parameter along the direction of composition gradient. Scanning Raman spectroscopy has been employed as a nondestructive tool to characterize the composition-spread films. Raman spectra showed the variation of the structural, Jahn Teller distortions and the presence of coexisting phases at particular compositions that are in agreement with the previous observation on the single-crystal samples. Raman spectra on the continuous composition-spread film also reveal the effect of disorder and strain on the compositions

Enhancement of magnetoresistance in manganite multilayers

Magnanite multilayers have been fabricated using La0.67Ca0.33MnO3 as the ferromagnetic layer and Pr0.7Ca0.3MnO3 and Nd0.5Ca0.5MnO3 as the spacer layers. All the multilayers were grown on LaAlO3 (100) by pulse laser deposition. An enhanced magnetoresistnace (defined (RH- R0)/R0) of more than 98% is observed in these multilayers. Also a low field magnetoresistance of 41% at 5000 Oe is observed in these multilayer films. The enhanced MR is attributed to the induced double exchange in the spacer layer, which is giving rise to more number of conducting carriers. This is compared by replacing the spacer layer with LaMnO3 where Mn exists only in 3+ state and no enhancement is observed in the La0.67Ca0.33MnO3 / LaMnO3 multilayers as double exchange mechanism can not be induced by external magnetic fields.Comment: 13 pages, 5 Figure